Plastic Film-Laminated Steel Sheets
Polyolefin-based plastic film-laminated steel sheets
HISHIMETALTM PO
HISHIMETAL PO incorporates galvanized steel sheets, stainless steel sheets, and aluminum alloy sheets as a base material.
HISHIMETAL PO is a composite material produced by laminating a polyolefin-based film onto the base material.
This material is used for interior and door etc.
Characteristics
- This material can be customized with the same variety of patterns and embossings as with PVC.
- This material has excellent chemical and solvent resistance.
Applications
- Interior applications
Curtain rails, closets, etc. - Exterior applications
Doors, etc. - Light electrical appliances
- Other
- Curtain rails
- Closet doors
Manufacturing Range and Order Conditions
-
Lot
A lot of 2.5 tons or more is required to order a product having the same specifications such as the same sheet thickness, width, color and embossing.
* Please order in lots of at least 2.5 tons as special request lots smaller than this will require an extra fee. -
Lead times
The standard lead time is 30 to 45 days. This can vary depending on the specification of the order.* Specifications of new orders requires a confirmation procedure, and so we recommend placing new orders as early as possible.
Performance
* Table can be scrolled horizontally
Specific test | Test conditions | Criteria | HISHIMETAL PO | |
---|---|---|---|---|
Adhesion | Conformal Erichsen 6 mm extrusion |
25±5°C | No separation | Nothing abnormal |
Bendability | Adhesion and bending test | 25±5°C, 0T | No cracking, breakage, and separation | Nothing abnormal |
Processability at low temperature | 90° bend test | 0±1°C, R=2 | No cracking, breakage, and separation | Nothing abnormal |
Resistance to boiling water | Dipping in boiling water | Submerged in water for 5 minutes after 60 minutes of immersion | No shrinkage, cracking, breakage, creasing, separation, and marked fading | Nothing abnormal |
Chemical resistance | 5-minute immersion (20±2°C) |
10% hydrochloric acid | No rust, stain, and marked fading | Nothing abnormal |
Saturated calcium hydroxide | ||||
10% sulfuric acid | ||||
Aqueous solution of sodium hydroxide (100 g/L) | ||||
Ethanol | ||||
Kerosene | ||||
Corrosion resistance | Complies with salt spray test JIS Z 2371 |
JIS K 6744 Type B: 1,000 hours |
No rust | Nothing abnormal |
*1 The data described above represents the specified values in our company and does not represent guaranteed values.
*2 Please contact us to inquire on the certification of fire-resistant materials.
Contact Us
Mitsubishi Chemical Infratec Co.,Ltd.
Designed materials Department
Designed materials Department
Designed Materials
Plastic Film-Laminated Steel Sheets
HISHIMETAL™ PO
HISHIMETAL™ PO